Basic Info.
MGO Content
0.2-1.3%
Application
Refractory Furnace Lining Insulation Materials
Density (Kg/M³ )
2.2-3.15g/cm3
Feature 1
Low Thermal Conductivity,Low Heat Storage
Feature 2
Good Thermal Shock Resistance
Feature 3
Reasonable Price
Transport Package
Standard One
Specification
Customized
Trademark
TK BRICKS
Origin
China
HS Code
381600000
Production Capacity
3000000 PCS Per Month
Product Description
Heat resistant Silicon nitride bonded silicon carbide refractory bricks
Silicon Carbide bricks is made of high quality SIC (72%~99%)and bonded by clay, It has the following features:High thermal conductivity,
high bending strength, good thermal shock resistance. Stable chemical performance,
high cold crushing strength, good anti corrosion ability.
The products are widely used in high temperature furnace lining (furnace bottom and hearth,
furnace body, etc.), smelting non-ferrous metal furnace lining.
Features:
1. High temperature resistant
2. Various sizes available
3. Competitive prices
4. Small tolorence: +-0.005mm
5. Good quality
6. Exact delivery time
| Item | RbSIC | SiSIC |
| Purity(%) | > 98 | >90 |
| Density(g/cm3 ) | 3.1-3.2 | >3.05 |
| Granularity(um) | 0.5-0.7 | 8--20 |
| Hardness(HRA) | ≥90 | ≥90 |
| Bending strength(MPa) | 400-580 | 350-450 |
| Compressive strength (MPa) | 3900 | >2500 |
| Fracture strength (MPa) | 3.05-4.6 | 4.3 |
| Modulus of elasticity(GPa) | 380-410 | 420 |
| Thermal comductivity | 102.6 | 35-110 |
| Coefficient of thermal expansion(1/ºC) | 4.02×10-6 | 4.3×10-6 |
| Poisson's ratio | 0.14 | 0.15 |
| Open porosity (%) | 7--8 | <0.1 |
| Temperature of application (ºC) | 1800 | 1410 |
| Item | SSIC |
| SIC Purity(%) | >98 |
| Bulk Density(g/cm3 ) | 3.06-3.15 |
| Max. Service Temp.(ºC) | 1800 |
| Compressive strength (Mpa) | ≥3900 |
| Bending strength(MPa) | 400-580 |
| Fracture strength(MPa) | 3.05-4.6 |
| Young's modulus(Gpa) | 380-410 |
| Thermal conductivity W/MK | 102.6 |
| Thermal expansion a(1/ºC) | 4.02x10 |
| Poisson's ratio | 0.14 |
| Apparent porosity % | 0 |